Filterpapier

Technical papers, smooth/ Grade H079

Made of 100 % cotton linters Ash-free (ash content = 0.01 % according to DIN 540370) Wet-strengthened Color-coded box for easy selection Very slow filtering Fine-pore 100 sheets per pack

Recommended for testing spectacle frames and sunglasses for nickel release, EN 16128:2015 Made of polyethylene coated cellulose Weight: 187 g/m² Water Capacity of 300% 480 mm x 600 mm sheets 100 sheets per pack

Made of 100 % cotton linters Ash-free (ash content = 0.01 % according to DIN 540370) Wet-strengthened Color-coded box for easy selection Very slow filtering very fine-pore 100 sheets per pack

Technical specifications:- Made of cotton linters- Low-nitrogen and nitrates content- Ash content ≤ 0.06 %- Weight: 87 g/cm²- Thickness: 0.18 mm- No additives, such as wet-strenghening Example of applications:- Determination of nitrogen content in soils- Malt filtration according to EBC standards

Made of > 95 % α-cellulose Ash content below 0.1 % according to DIN 54370 Wide pore, loose structure Fast filtering 430 mm x 500 mm sheets 100 sheets per pack

Made of > 95 % α-cellulose Ash content below 0.1 % according to DIN 54370 Very fine pore, very dense Very slow filtering 460 mm x 570 mm sheets 100 sheets per pack

Technical specifications:- Made of cotton linters- Low-nitrogen and nitrates content- Ash content ≤ 0.06 %- Weight: 97 g/cm²- Thickness: 0.19 mm- No additives, such as wet-strenghening Example of applications:- Determination of nitrogen content in soils

Made from cotton linters and refined pulp with > 95% alpha-cellulose content Weight of 360 g/m² Thickness of 0.75 mm Wet bursting strength of ≥ 200 kPa Air resistance of 30 mbar 375 mm x 500 mm square sheets 125 sheets per pack

This paper grade is generally used for analytical and technical purposes.

This paper grade is generally used for analytical and technical purposes.

This smooth yellow paper grade satisfies the requirements for the determination of dermination capability according to ISTA (International Seed Testing Association) and is ideal for ensuring optimal moisture content for the most diverse types of seeds and germination forms. The pH ranges between 6.0 and 7.5, it is wet-strengthened and the special structure prevents fine seed...

Made of refined pulp and cotton linters with an > 95% α-cellulose content Ash content between 0.1 - 0.15% Wet-strengthened

Technische Papiere, glatt/ Sorte 57/NB

Filter boards/ Grade H182

Filter boards/ Grade H182

Application Example Petrochemical industry: Filtration of viscous solutions to retain the biggest particles before further analysis with a viscosimetry

Application Example Petrochemical industry: Filtration of viscous solutions to retain the biggest particles before further analysis with a viscosimetry

Application Example Testing of mortars containing mineral binders; determinatin of water retentivity of freshly mixed mortar by the filterplate method according to DIN 18555-7

Made of refined pulp and cotton linters with an > 95% α-cellulose content Ash content between 0.1 - 0.15% Wet-strengthened

Made of refined pulp and cotton linters with an > 95% α-cellulose content Ash content between 0.1 - 0.15% Wet-strengthened

Made of refined pulp and cotton linters with an > 95% α-cellulose content Ash content between 0.1 - 0.15% Wet-strengthened

Made of refined pulp and cotton linters with an > 95% α-cellulose content Ash content between 0.1 - 0.15% Wet-strengthened

Made of refined pulp and cotton linters with an > 95% α-cellulose content Ash content between 0.1 - 0.15% Wet-strengthened